Effect of dentin preparation mode on the bond strength between human dentin and different resin cements

Abstract The aim was to evaluate the influence of different dentin preparation mode in the smear layer characteristics (SL), hybrid layer (HL), and microtensile bond strength (µTBS) to dentin with two resin cements. The occlusal dentin of 120 third molars was exposed. The teeth were divided into 4 groups (n=30) according to the dentin preparation mode: 1- fine grain diamond bur; 2- coarse grain diamond bur; 3- multi laminate carbide steel bur; and, 4- ultrasonic CV Dentus diamond bur. Each treated dentin group was divided into 2 sub-groups (n=15) according to the resin cement: (1) RelyX U200 and (2) RelyX ARC. Resin composite blocks were cemented on dentin. After storage at 37o C for 24 h, beams with a cross section area of 1.0 mm2 were obtained, and tested in a universal testing machine at a crosshead speed of 0.5 mm/min. Two additional teeth for each sub-group were prepared to analyze the SL and HL on a scanning electron microscopy. According to Kruskal-Wallis test and Dunn tests, there was no significant difference in µTBS among the rotary instruments within each resin cement group. RelyX ARC obtained higher µTBS values compared to RelyX U200 (p<0.05). RelyX ARC formed evident HL, which was not observed for RelyX U200. The dentin mode preparation did not influence the µTBS of the resin cements. The SL was different for all instruments. The cementing agent is more determinant in the hybrid layer formation and bond strength to dentin than the instruments applied on dentin.

Resumo O objetivo deste estudo foi avaliar a influência de diferentes modos de preparação da dentina nas características da smear layer (SL), da camada híbrida (CH) e na resistência de união à microtração (RUµT) à dentina com dois cimentos resinosos. A dentina oclusal de 120 terceiros molares humanos foi exposta. Os dentes foram divididos em 4 grupos (n=30) de acordo com o modo de preparação da dentina: 1 - ponta diamantada de granulação fina; 2 - ponta diamantada de granulação grossa; 3 - ponta de carboneto de aço multilaminada; 4 - ponta diamantada ultrassônica. Cada grupo foi subdividido em dois subgrupos (n=15) de acordo com o cimento resinoso: (1) RelyX U200 e (2) RelyX ARC. Blocos de resina composta foram cimentados na dentina. Após armazenamento a 37 °C por 24 h, as amostras foram cortadas para obter palitos com área de 1,0 mm2, os quais foram testados em máquina de ensaio universal com velocidade de 0,5 mm/min. Dois dentes adicionais por subgrupo foram preparados para analisar as características da SL e da CH em microscópio eletrônico de varredura. De acordo com o teste de Kruskal-Wallis e o teste de Dunn, não houve diferença significativa na RUµT entre os instrumentos rotatórios para cada cimento resinoso. RelyX ARC obteve maiores valores de RUµT em comparação ao RelyX U200 (p<0,05). RelyX ARC formou uma CH evidente, o que não foi observado para o RelyX U200. O modo de preparação da dentina não influenciou na RUµT dos cimentos resinosos. A SL foi diferente para todos os instrumentos. O agente de cimentação foi mais determinante na formação da camada híbrida e na resistência de união do que os instrumentos utilizados para preparar a dentina.

Plataforma reduzida, uma solução estética. Revisão de Literatura / Platform switching: an aesthetic solution. Literature review

O objetivo da presente revisão da literatura foi avaliar a influência do uso de plataformas reduzidas sobre os níveis de crista óssea considerando-se o tipo de conexão, carga mastigatória e necessidades estéticas. De acordo com a literatura pesquisada, concluiu-se que a plataforma reduzida mantém a crista óssea em níveis satisfatórios em torno de implante tanto hexágono externo, interno e cone Morse, implantes com carga imediata com plataforma reduzida em regiões que não sofrem cargas excessivas mantêm a crista óssea em níveis satisfatórios. A utilização de plataforma reduzida em áreas estéticas é uma opção para manter o nível da crista óssea, garantindo a manutenção das papilas e melhorando os contornos dos tecidos peri-implantares.

The purpose of this literature review was to evaluate the influence of using platforms switching considering the levels of bone crest, type of connection, masticatory load and aesthetic needs. According to the literature, it was concluded that the platform switching keeps the bone crest at satisfactory levels around the implant both external hexagon, internal hexagon and Morse taper, with immediate loading implants with platform switching in regions that do not suffer from excessive loads maintains the crest bone at satisfactory levels. The use of the platform switching in aesthetic areas is an option to keep the bone crest level, ensuring the maintenance of the papillae and improving tissue contours periimplant.

Influence of ceramic primers on microshear bond strength between resin cements and zirconia-based ceramic

This study evaluated the effect of a coupling agent ceramic primer (CP) on the microshear bond strength (ìsbs) between luting cements and zirconia-based ceramic. Methods: Zirconia discs (Cercon) were made and finished with silicon carbide paper and submitted to air abrasion using 50 μm aluminum oxide particles (Al2O3) under 4 bar pressure. Zirconia disks were randomly assigned to four groups (n=10): (G1) ResiCem luting cement + Porcelain Primer, (G2) ResiCemluting cement only, (G3) Clearfil Esthetic Cement + Clearfil Ceramic Primer and (G4) Clearfil Esthetic Cement only. The luting cements were prepared according to manufacturers’ recommendations and inserted in an elastomeric mold positioned onto a zirconia disc. Each specimen was photoactivated by 20 s. The specimens were stored at 100% relative humidity and 37ºC for 24 h. The ìsbs test was performed using universal testing machine at a crosshead speed of 0.5 mm/min. An optical microscope was used to analyze the failure modes and illustrative images were captured with a scanning electron microscope. The ìsbs data were analyzed by two-way ANOVA (p<0.05). Results: No significant difference was found among the four groups G1 (17.4±6.8), G2 (17.1±5.5), G3 (15.6±5.5) and G4 (14.2±3.5), all of which showed 100% of adhesive failures. Conclusions: CP showed no increase in the ìsbs between zirconia-based ceramic and resin luting cements.

O condicionamento ácido prévio ainda é indispensável para a odontologia adesiva? / Is previous total etching still indispensable for the adhesive dentistry?

O objetivo deste trabalho foi avaliar as características dos sistemas adesivos disponíveis atualmente considerando a aplicação ou não do condicionamento prévio com ácido fosfórico. O conhecimento das estruturas e o tratamento adequado do substrato dental são fundamentais para utilização dos adesivos convencionais. Os sistemas adesivos autocondicionantes possuem técnica simplificada dispensando o condicionamento ácido prévio. O profissional deverá ter conhecimento dos mecanismos de adesão ao substrato dental, experiência clínica e domínio da técnica de aplicação do adesivo escolhido. O condicionamento ácido prévio não deve ser considerado indispensável na Odontologia adesiva atual.

Avaliação in vitro da infiltração marginal em inlays de resinas compostas em função de tipos de fontes de luz e agentes de cimentação / Evaluation in vitro of composite resin inlays in function of types of light units and luting agent

O objetivo deste trabalho foi avaliar a infiltração marginal da resina Flow Filtek e do cimento resinoso dual RelyX na fixação de inlays de cerômeros fotoativados com LEDs e Luz Halógena. Foram selecionados 32 dentes íntegros recém-extraídos armazenados em solução de soro fisiológico no freezer, divididos em quatro grupos: Grupo I - aparelho Elipar FreeLight e resina Flow Filtek; Grupo II - aparelho Ultralux e Resina Flow Filtek; Grupo III - aparelho Elipar FreeLight e cimento resinoso RelyX e Grupo IV - aparelho Ultralux e cimento resinoso RelyX. Foram feitos 64 preparos cavitários com término em esmalte e cemento a 1 mm acima e abaixo da junção amelo-cementária respectivamente. As inlays foram jateadas internamente com óxido de alumínio de 100 um com 40 Bar de pressão e, posteriormente foi feito o condicionamento das superfícies das inlays com ácido fosfórico a 37 percento durante 60 segundos, as quais foram lavadas e silanizadas. Após o condicionamento das inlays, foi feito o preparo da superfície dental com ácido fosfórico a 37 percento durante 15 segundos, as quais foram lavadas, secas com papel absorvente, tendo sido aplicado o...